E71t1 Rutile Flux Cored Welding Wire for High Tensile Steels

• Customization: Available
• Type: Flux-cored Wire
• Material: High Tensile Strength Steels
• Model NO.: E71T1
• Flux Containing: Containing Flux
• Slag Characteristic: Acidic
• Extended Length: 15-25mm
• Transport Package: Customized
• Specification: 1/5/15/20 KG
• Trademark: JINYUAN
• Origin: China
• HS Code: 7229200000
• Production Capacity: 1000 Tons Per Month

Product Description

It shows excellent welding performance and higher efficiency in welding.Vertical down welding could be applied.It is widely used in structures fabricated by equivalent mild steels and 490MPa grade high tensile strength steels, such as ships,pressure vessels,machineries ,petrochemical industry equipments,bridges and so on.

Basic Info.

Model NO.	E71T1
Size(mm)	1.0/1.2/1.4/1.6
Slag Characteristic	Acidic
Shielded Gas	CO2
Type Of Current	DC+
Specification	1/5/15/20kg
Flux Containing	Containing Flux
Application	Structures fabricated by equivalent mild steels and 490Mpa grade high tensile strength steels. such as ships, pressure vessels, machineries, petrochemical industry equipments and so on.
Origin	China

Product Specification

E71T1
E71T1 Welding Wire Chemical Composition of Deposited Metal (%)
Composition	C	Mn	Si	S	P
Standard	≤0.18	≤1.75	≤0.90	≤0.03	≤0.03
Typical	0.055	1.35	0.40	0.009	0.018

 

E71T1 Welding Wire Mechanical Properties of Deposited Metal(AW)
	Yield Strength ReH(Mpa)	Tensile Strength Rm (Mpa)	Elongation A4(%)	Impact Value(J)	Shield Gas
				-20ºC	CO2
Standard	≥400	≥480	≥22	≥27	purity≥99.98%
Typical	440	535	32	110

 

E71TGS
E71TGS Welding Wire Chemical Composition of Deposited Metal (%)
items	C	Mn	Si	S	P	Ni	Al
Standard value	-	≤1.75	≤0.92	≤0.03	≤0.03	≤0.50	≤1.80

 

E71TGS Welding Wire Mechanical Properties of Deposited Metal(AW)
Test items	Yield Strength Rm(Mpa)	Tensile Strength Rm(Mpa)	Elongation A4(%)
Standard valve	≥400	≥480	-

Attention
The flow rate of shield gas should within 20L-50L/min in welding
The wire extention should be 15mm-25mm
The surfaces to be welded must be cleaned away impurities of oil contamination, rust,moisture and so on.