Factory Direct Sales Stainless Steel Welding Electrodes Aws E308-16 E308L-16 Welding Rod

• Customization: Available
• Type: S (Chromium Nickel Austenitic Stainless Steel Electrode)
• Material: Stainless Steel
• Model NO.: E308-16 E308L-16
• Diameter: 2.0mm-5.0mm
• Length: 300-400mm
• Welding Core Type: Stainless Steel
• Electrode Coating Type: Titanium Calcium
• Slag Characteristic: Acidic
• Stainless Steel Welding Rod Type: Chromium Stainless Steel
• Function: Low Hydrogen Type Electrode, Gravity Electrode, Moisture-Proof Electrode
• Welding Power: AC/DC
• Transport Package: Carton
• Specification: 3.2x350mm 2.5x300mm 4.0/5.0x400
• Trademark: JINYUAN
• Origin: Hebei, China
• HS Code: 83113000

Product Description

Product Description

 

E308L-16 Welding Electrode

 

Applications :

For welding of ultra-low carbon's SuS304L stainless steel, also can be used for Sus321 and other corrosion resistant stainless steel structure.

Attention:

1.The electrode must be re-dry by 320ºC-350ºC for 1 hour before welding.
2.The rust, oil, water and other impurities of the weld area must be removed before welding.
3.DC*is better than AC, lower heat input is suggested, the temperature of preheat and interpass keep under 150ºC.

Chemical Composition of All Weld Meta(%)

items	C	Mn	Si	Cr	Ni	Mo	Cu	S	P
Requirements	≤0.04	0.50-2.50	≤1.00	18.0-21.0	9.0-12.0	≤0.75	≤0.75	≤0.03	≤0.04
Typical Results	0.029	0.94	0.73	19.60	9.60	0.08	0.10	0.010	0.028

 Mechanical Properties of Deposited Metal (AW)

	Tensile Strength Rm (MPa)	Elongation A(%)
Requirements	≥510	≥30
Typical Results	578	41

E308-16 Welding Electrode

 

Applications :

For welding of the working temperature is less than 300 ºC corrosion resistant stainless steel structure, such as SUS304 etc.
 

 

Attention:

1.The electrode must be re-dry by 320ºC-350ºC for 1 hour before welding.

2.The rust, oil, water and other impurities of the weld area must be removed before welding.
3.DC*is better than AC, lower heat input is suggested, the temperature of preheat and interpass keep under 150ºC.
 

Chemical Composition Of Deposited Metal (%)

items	C	Mn	Si	Cr	Ni	Mo	Cu	S	p
Requirements	≤0.08	0.5-2.5	≤1.00	18.0-21.0	9.0-11.0	≤0.75	≤0.75	≤0.03	≤0.04
Typical Results	0.06	0.87	0.67	20.00	9.50	0.09	0.08	0.010	0.025

Mechanical Properties of Deposited Metal (AW)

items	Tensile Strength Rm (MPa)	Elongation A4(%)
Requirements	≥550	≥30
Typical Results	596	43

 

Notice

1) The rod should be baked at 300ºC -350ºC for 1 hour before use.
2) The surfaces to be welded must be cleaned away impurities of oil contamination, moisture and so on.
3) Smaller current and short arc are recommended in welding and weave beads no wider than 2.5 times of the diameter of the core rod is better.
 

Detailed Photos

Certifications

 

Company Profile

 

 

FAQ

1. Are you manufacturer?
We are manufacturer of galvanized wire, annealed wire, barbed wire, razor wire, welded wire mesh, hexagonal wire mesh, chain link fence, iron nails, steel nails, drywall screw, welding electrode, welding wire.

2. How can we guarantee quality?
Always final Inspection before shipment.

3.What can you buy from us?
Galvanized Wire,Annealed Wire,Nails,Welding Electrode,Wire Meshes.

4. Why should you buy from us not from other suppliers?
1). 22 Years Production Experirance
2). Quality Checking Before Shipment
3). 8 Production Line and 60 Drawing Wire Machine
4). Short Delivery Time
5). OEM