Durable Lime-Titania Stainless Steel Welding Electrode E308L-16 From China

• Customization: Available
• Type: H (Heat Resistant Low Alloy Steel/ Stainless Steel Electrode)
• Material: Stainless Steel
• Model NO.: E308L-16
• Diameter: 2.0~5.0mm
• Length: 300-400mm
• Welding Core Type: Stainless Steel
• Electrode Coating Type: Titanium Calcium
• Slag Characteristic: Acidic
• Stainless Steel Welding Rod Type: Chromium Stainless Steel
• Function: Low Hydrogen Type Electrode, Gravity Electrode, Moisture-Proof Electrode
• Welding Power: DC/AC
• Transport Package: Customized
• Specification: 3.2x350mm 2.5x300mm 4.0/5.0x400
• Trademark: JINYUAN
• Origin: China
• HS Code: 831110000
• Production Capacity: 1000 Tons Per Month

Product Description

Crafted entirely from premium-grade steel, our product boasts exceptional resistance to rust, ensuring a sleek, polished surface and an impressively extended lifespan.
With cutting-edge production technology, our products exhibit a consistently stable structure, where meticulous attention is given to each and every detail.

We employ state-of-the-art testing equipment to conduct rigorous assessments, upholding the highest standards of product quality assurance.

Basic Info.

Model NO.	E308-16, E308L-16, E309-16, E309L-16,E312-16,E316L-16
Length	300-400mm
Electrode Coating Type	Titanium Calcium
Welding Power	AC/DC
Origin	China
Diameter	2.0~5.0mm
Welding Core Type	Stainless Steel
Transport Package	Carton
Function	For welding of the working temperature is less than 300 ºC corrosion resistant stainless steel structure, such as SUS304 etc..
Trademark	JINYUAN

Product Specification

E308L-16
Chemical Composition Of Deposited Metal (%)
items	C	Mn	Si	Cr	Ni	Mo	Cu	S	P
Requirements	≤0.04	0.5-2.50	≤1.00	18.0-21.0	9.0-11.0	≤0.75	≤0.15	≤0.03	≤0.04
Typical Results	0.029	0.86	0.63	19.80	9.60	0.10	0.022	0.012	0.024

Mechanical Properties of Deposited Metal (AW)
items	Tensile Strength Rm(Mpa)	Elongation A4(%)
Requirements	≥520	≥35
Typical Results	575	46

E308-16
Chemical Composition Of Deposited Metal (%)
items	C	Mn	Si	Cr	Ni	Mo	Cu	S	P
Requirements	≤0.08	0.5-2.5	≤1.00	18.0-21.0	9.0-11.0	≤0.75	≤0.75	≤0.03	≤0.04
Typical Results	0.06	0.87	0.67	20.00	9.50	0.09	0.08	0.010	0.025

Mechanical Properties of Deposited Metal (AW)
items	Tensile Strength Rm (MPa)	Elongation A4(%)
Requirements	≥550	≥30
Typical Results	596	43

 

E309-16
Chemical Composition Of Deposited Metal (%)
items	C	Mn	Si	Cr	Ni	Mo	Cu	S	P
Requirements	≤0.15	0.5-2.50	≤1.00	22.0-25.0	12.0-14.0	≤0.75	≤0.75	≤0.03	≤0.04
Typical Results	0.06	0.89	0.69	24.05	12.5	0.10	0.08	0.010	0.028

Mechanical Properties of Deposited Metal (AW)
items	Tensile Strength Rm (MPa)	Elongation A4(%)
Requirements	≥550	≥25
Typical Results	600	38

E309L-16
Chemical Composition Of Deposited Metal (%)
items	C	Mn	Si	Cr	Ni	Mo	Cu	S	P
Requirements	≤0.15	0.5-2.50	≤1.00	28.0-32.0	8-10.5	≤0.75	≤0.75	≤0.03	≤0.04
Typical Results	0.085	1.11	0.78	29.39	9.97	0.16	0.2	0.011	0.028

Mechanical Properties of Deposited Metal (AW)
items	Tensile Strength Rm (MPa)	Elongation A4(%)
Requirements	≥510	≥25
Typical Results	565	41

E312-16
Chemical Composition Of Deposited Metal (%)
items	C	Mn	Si	Cr	Ni	Mo	Cu	S	P
Requirements	≤0.15	0.5-2.50	≤1.00	28.0-32.0	8-10.5	≤0.75	≤0.75	≤0.03	≤0.04
Typical Results	0.085	1.11	0.78	29.39	9.97	0.16	0.2	0.011	0.028

Mechanical Properties of Deposited Metal (AW)
items	Tensile Strength Rm (MPa)	Elongation A4(%)
Requirements	≥660	≥15
Typical Results	785	26

E316L-16
items	C	Mn	Si	Cr	Ni	Mo	Cu	S	P
Requirements	≤0.04	0.5-2.50	≤1.00	17.0-20.0	11-14	2-3	≤0.75	≤0.03	≤0.04
Typical Results	0.030	1.01	0.68	19.01	11.82	2.46	0.08	0.015	0.025

Mechanical Properties of Deposited Metal (AW)
items	Tensile Strength Rm (MPa)	Elongation A4(%)
Requirements	≥490	≥25
Typical Results	580	45

Attention:

1. Prior to welding, it is mandatory to re-dry the electrode at 320ºC-350ºC for a duration of 1 hour to ensure optimal performance.
2. Ensure the weld area is meticulously free from rust, oil, water, and any impurities before commencing the welding process.
3. While DC* is preferable over AC, it is advised to use lower heat input, maintaining preheat and interpass temperatures below 150ºC for best results.
Packing Details

 