| Customization: | Available |
|---|---|
| Type: | E (Carbon Steel Electrodes/ Low Alloy Steel Electrodes) |
| Material: | Carbon Steel |
|
Still deciding? Get samples of $ !
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| E6013 Welding Electrode | |
| Application | low carbon steel structure,especially for the welding of thin plate steel with short discontinuous weld and requirement of smooth welding pass. |
| Welding Position |
All Position.
PA, PB, PC, PD, PE, PF
|
| X-ray Inspection | II Level |
| Color | Grey, Blue, Red, White Yellow |
| Advantage |
1.Stable Arc
2. Little Spatter
3. Easily Remove Slag
4.Easy Reignition
5. Little Smoke
|
| Please check more details below. | |
| E6013 Welding Electrode Chemical Composition of Deposited Metal (%) | |||||||||
| Composition | C | Mn | Si | S | P | Ni | Cr | Mo | V |
| Guarantee Value | ≤0.10 | 0.32-0.55 | ≤0.30 | ≤0.030 | ≤0.035 | ≤0.30 | ≤0.20 | ≤0.30 | ≤0.08 |
| Typical Results | 0.08 | 0.37 | 0.18 | 0.020 | 0.025 | 0.030 | 0.035 | 0.005 | 0.004 |
| E6013 Welding Electrode Mechanical Properties of Deposited Metal | ||||
| Test Item | Rm (Mpa) | Rel/Rp0.2(Mpa) | A(%) | KV2(0ºC)(J) |
| Requirements | 440-560 | ≥355 | ≥22 | ≥47 |
| Typical Results | 500 | 430 | 27 | 80 |
| E6013 Welding Electrode Reference Current( AC, DC) | ||||||
| Diameter (mm) | 2.0 | 2.5 | 3.2 | 4.0 | 5.0 | 5.8 |
| Length(mm) | 300 | 300 | 350 | 400 | 400 | 400 |
| Welding Current (A) | 40-70 | 50-90 | 80-130 | 150-200 | 180-240 | 220-280 |
| E7018 Welding Electrode | |
| Features & Applications: Its nominal deposited efffciency is about 110%. The weld metal shows excellent low temperature toughness and high crack resistance. It is widely used in important structures fabricated by equivalent tensile strength mild steels or low ally steels such as ships, boilers, high pressure vessels, bridges, skyscrapers, offshore drilling platforms, nuclear power plants and so on. It has been appointed to be honor consumables by almost all nuclear power projects in China due to its faithworthy quality. |
|
| Notice: 1) The rod should be baked at 400ºC for 1-2 hours before use. 2) The surfaces to be welded must be cleaned away impurities of oil contamination, rust, moisture and so on. 3) Short Arc and narrow-gap welding is recommended. |
|
| E7018 Chemical Composition of All Weld Metal:(Wt.%) | |||||||||
| Items | C | Mn | Si | S | P | Ni | Cr | Mo | V |
| Requirements | ≤0.10 | 0.85-1.40 | ≤0.65 | ≤0.030 | ≤0.035 | ≤0.30 | ≤0.20 | ≤0.30 | ≤0.08 |
| Typical Results | 0.06 | 1.00 | 0.30 | 0.015 | 0.020 | 0.030 | 0.035 | 0.005 | 0.004 |
| E7018 Mechanical Properties of All Weld Metal | ||||
| Items | Rm (Mpa) | Rel/Rp0.2(Mpa) | A(%) | KV2((-30ºC)(J) |
| Requirements | 490-660 | ≥400 | ≥22 | ≥80 |
| Typical Results | 590 | 480 | 28 | 160 |
| E7018 Typical Operating Procedures:(AC or DC) | ||
| Diameter | Length | Electric Current |
| 2.5mm | 300mm | 60-100A |
| 3.2mm | 350mm | 100-150A |
| 4.0mm | 400mm | 170-210A |
| 5.0mm | 400mm | 210-250A |
| E6011 Welding Electrode | |
| Application | Low carbon steel structure such as Pipeline, Shipbuilding, Bridge |
| Welding Position |
All Position.
(especially for vertical-down position)
PA, PB, PC, PD, PE, PF, PG
|
| X-ray Inspection | II Level |
| Color | White Yellow |
| Advantage |
1.Stable Arc
2. Little Spatter
3. Easily Remove Slag
4.Easy Reignition
5. Little Smoke
6. Vertical-down Welding
|
| Please check more details below. | |
| E6011 Welding Electrode Chemical Composition of Deposited Metal (Wt.%) | |||||||||
| Composition | C | Mn | Si | S | P | Ni | Cr | Mo | V |
| Guarantee Value | ≤0.20 | ≤1.2 | ≤1.00 | ≤0.035 | ≤0.040 | ≤0.30 | ≤0.20 | ≤0.30 | ≤0.08 |
| Typical Results | 0.09 | 0.70 | 0.30 | 0.020 | 0.018 | 0.030 | 0.035 | 0.005 | 0.004 |
| E6011 Welding Electrode Mechanical Properties of All Weld Metal | ||||
| Test Item | Rm (Mpa) | Rel/Rp0.2(Mpa) | A(%) | KV2(0ºC)(J) |
| Requirements | ≥430 | ≥330 | ≥20 | ≥27(-30ºC) |
| Typical Results | 558 | 460 | 24.5 | 45 |
| E6011 Welding Electrode Reference Current( AC, DC) | ||||
| Diameter (mm) | 2.5 | 3.2 | 4.0 | 5.0 |
| Length(mm) | 350 | 350 | 400 | 400 |
| Welding Current (A) | 40-60 | 80-100 | 100-140 | 150-200 |
| E6010 Welding Electrode | |
| Features & Applications: It is mainly used for backing welding of substrate, root passes, ffller and cosmetic welding of mild steel pipes. It could be fashioned by one-side welding with back formation. |
|
Notice: 1) Good condition of packaging and storage for it is important. 2) Normally it does not need to re-dry. When it is damped seriously re-bake it at temperature of 70ºC -80ºC for 0.5-1 hour before welding. 3) To increase performance of welding, when using dia. 5.0mm one, bigger thrust and smaller current are recommended. |
|
| E6010 Chemical Composition of Deposited Metal (%) | |||||||||
| C | Mn | Si | S | P | Ni | Cr | Mo | V | |
| Standard | ≤0.20 | ≤1.20 | ≤1.00 | -- | -- | ≤0.30 | ≤0.20 | ≤0.30 | ≤0.08 |
| Typical | 0.091 | 0.55 | 0.17 | 0.010 | 0.011 | 0.011 | 0.022 | 0.001 | 0.01 |
| E6010 Mechanical Properties of Deposited Metal (AW) | ||||
| Tensile Strength Rm(Mpa) |
Yield strength ReL(Mpa) |
Elongation A4(%) |
Impact Value (J) | |
| -30ºC | ||||
| Standard | ≥430 | ≥330 | ≥22 | ≥27 |
| Typical | 500 | 400 | 29 | 80 |
| E6010 Sizes, Pieces & Recommended Current (DC+ ) | |||||
| Size (mm) | 2.5 x 300 | 3.2 x 350 | 4.0 x 350 | 5.0 x 350 | |
| Pieces (5kg) | ≈328 | ≈185 | ≈120 | ≈76 | |
| Current (A) | F, H | 60-90 | 70-110 | 110-150 | 150-200 |
| OH, VD | 50-80 | 60-100 | 100-140 | 140-180 | |
| E7014 Welding Electrode |
| Features & Applications: Its nominal deposited efffciency is about 110% and it is used for welding structures fabricated by equivalent tensile strength mild steels or low alloy steels, such as machineries, vehicles and so on. |
| Notice: Normally the rod does not need to re-dry in case it is affected with damp seriously re-bake it at 150ºC for 30-60 minutes before use. |
| E7014 Chemical Composition of Deposited Metal (%) | |||||||||
| C | Mn* | Si | S | P | Cr* | Ni* | Mo* | V* | |
| Standard | - | ≤1.25 | ≤0.90 | ≤0.035 | ≤0.035 | ≤0.20 | ≤0.30 | ≤0.30 | ≤0.08 |
| Typical | 0.065 | 0.60 | 0.40 | 0.020 | 0.025 | 0.001 | 0.011 | 0.013 | 0.06 |
| E7014 Mechanical Properties of Deposited Metal (AW) | |||
| Tensile Strength Rm(Mpa) |
Yield strength ReL(Mpa) |
Elongation A4(%) |
|
| Typical | 560 | 480 | 25 |
| Standard | ≥490 | ≥400 | ≥17 |
| E7014 Sizes & Recommended Current (AC or DC) | |||||
| Size (mm) | 2.5 x 300 | 3.2 x 350 | 4.0 x 400 | 5.0 x 400 | |
| Current (A) | F, H | 60-90 | 80-130 | 150-190 | 180-250 |
| V,OH | 50-80 | 70-120 | 130-170 | - | |
| E7016 Welding Electrode |
| Features & Applications: It is used for main parts of ships, e.g. boilers, pressure vessels and pipes made by equivalent tensile strength steels, such as A, B, D, E, AH36, DH36 or EH36. Also it can be applied to homothetic strength structures of bridges, machineries, constructions, vehicles and so on. The weld metal has good performance of plasticity, impact toughness and crack resistance. |
| Notice: 1) The rod should be baked at 350ºC for 1 hour before use. 2) The surfaces to be welded must be cleaned away impurities of oil contamination, rust, moisture and so on. 3) Short arc and narrow-gap welding is recommended. |
| E7016 Chemical Composition of Deposited Metal (%) | |||||||||
| C | Mn* | Si | S | P | Cr* | Ni* | Mo* | V* | |
| Standard | ≤0.15 | ≤1.60 | ≤0.75 | ≤0.035 | ≤0.035 | ≤0.20 | ≤0.30 | ≤0.30 | ≤0.08 |
| Typical | 0.070 | 1.12 | 0.54 | 0.007 | 0.018 | 0.027 | 0.006 | 0.003 | 0.016 |
| E7016 Mechanical Properties of Deposited Metal (AW) | |||||
| Yield strength ReH(Mpa) |
Tensile strength Rm(Mpa) |
Elongation A4(%) |
Impact Value (J) | ||
| -20ºC | -30ºC | ||||
| Standard | ≥375 | 490-660 | ≥22 | ≥47 | ≥27 |
| Typical | 450 | 550 | 30 | 185 | 170 |
| E7016 Sizes & Recommended Current (DC+ or AC open circuit voltage ≥70V) | |||||
| Size (mm) | 2.5 x 300 | 3.2 x 350 | 4.0 x 400 | 5.0 x 400 | |
| Current (A) | F, H | 70-110 | 100-140 | 140-180 | 180-230 |
| V,OH | 50-80 | 80-110 | 130-170 | - | |
| Chemical Composition of Deposited Metal (%) | ||||||||
| Institute | CCS | LR | ABS | BV | GL | DNV | NK | BKI |
| Grade | 3YH10 | 3Ym, H15 | 3Y | 3YHH | 3YH10 | 3YH10 | KMW53H10 | 3YH10 |
1. Are you manufacturer?
We have more than 20 years produce experience. And we are manufacturer of galvanized wire, annealed wire, barbed wire, razor wire, welded wire mesh, hexagonal wire mesh, chain link fence, iron nails, steel nails, drywall screw, welding electrode, welding wire.Welcome to inquiry.
2. how can we guarantee quality?
Always a pre-production sample before mass production;
Always final Inspection before shipment;
3.what can you buy from us?
Galvanized Wire,Annealed Wire,Nails,Welding Electrode,Wire Meshes
4. why should you buy from us not from other suppliers?
1). High Quality Products
2). 22 Years Production Experirance
3). 8 Production Line and 60 Drawing Wire Machine