Manufacturer Stainless Steel Welding Electrode Welding Rod Aws E309-16

• Customization: Available
• Type: H (Heat Resistant Low Alloy Steel/ Stainless Steel Electrode)
• Material: Stainless Steel
• Model NO.: E309-16
• Diameter: 2.0~5.0mm
• Length: 300-400mm
• Welding Core Type: Stainless Steel
• Electrode Coating Type: Titanium Calcium
• Slag Characteristic: Acidic
• Stainless Steel Welding Rod Type: Chromium Stainless Steel
• Function: Low Hydrogen Type Electrode, Gravity Electrode, Moisture-Proof Electrode
• Welding Power: DC/AC
• Transport Package: Customized
• Specification: 3.2x350mm 2.5x300mm 4.0/5.0x400
• Trademark: JINYUAN
• Origin: China
• HS Code: 8311100000
• Production Capacity: 1000 Tons Per Month

Product Description

The whole is made of high-quality steel, which is not easy to rust, has a smooth surface and a long service life.
Professional production technology, stable structure, attention to every detail.

Use professional testing equipment to strictly test products to ensure product quality.

Basic Info.

Model NO.	E308-16, E308L-16, E309-16, E309L-16,E312-16,E316L-16
Length	300-400mm
Electrode Coating Type	Titanium Calcium
Welding Power	AC/DC
Origin	China
Diameter	2.0~5.0mm
Welding Core Type	Stainless Steel
Transport Package	Carton
Function	For welding of the working temperature is less than 300 ºC corrosion resistant stainless steel structure, such as SUS304 etc..
Trademark	JINYUAN

Product Specification

E309-16
Chemical Composition Of Deposited Metal (%)
items	C	Mn	Si	Cr	Ni	Mo	Cu	S	P
Requirements	≤0.15	0.5-2.50	≤1.00	22.0-25.0	12.0-14.0	≤0.75	≤0.75	≤0.03	≤0.04
Typical Results	0.06	0.89	0.69	24.05	12.5	0.10	0.08	0.010	0.028

Mechanical Properties of Deposited Metal (AW)
items	Tensile Strength Rm (MPa)	Elongation A4(%)
Requirements	≥550	≥25
Typical Results	600	38

 

E308-16
Chemical Composition Of Deposited Metal (%)
items	C	Mn	Si	Cr	Ni	Mo	Cu	S	P
Requirements	≤0.08	0.5-2.5	≤1.00	18.0-21.0	9.0-11.0	≤0.75	≤0.75	≤0.03	≤0.04
Typical Results	0.06	0.87	0.67	20.00	9.50	0.09	0.08	0.010	0.025

Mechanical Properties of Deposited Metal (AW)
items	Tensile Strength Rm (MPa)	Elongation A4(%)
Requirements	≥550	≥30
Typical Results	596	43

 

E308L-16
Chemical Composition Of Deposited Metal (%)
items	C	Mn	Si	Cr	Ni	Mo	Cu	S	P
Requirements	≤0.04	0.5-2.50	≤1.00	18.0-21.0	9.0-11.0	≤0.75	≤0.15	≤0.03	≤0.04
Typical Results	0.029	0.86	0.63	19.80	9.60	0.10	0.022	0.012	0.024

 

Mechanical Properties of Deposited Metal (AW)
items	Tensile Strength Rm(Mpa)	Elongation A4(%)
Requirements	≥520	≥35
Typical Results	575	46

 

E309L-16
Chemical Composition Of Deposited Metal (%)
items	C	Mn	Si	Cr	Ni	Mo	Cu	S	P
Requirements	≤0.15	0.5-2.50	≤1.00	28.0-32.0	8-10.5	≤0.75	≤0.75	≤0.03	≤0.04
Typical Results	0.085	1.11	0.78	29.39	9.97	0.16	0.2	0.011	0.028

Mechanical Properties of Deposited Metal (AW)
items	Tensile Strength Rm (MPa)	Elongation A4(%)
Requirements	≥510	≥25
Typical Results	565	41

 

E312-16
Chemical Composition Of Deposited Metal (%)
items	C	Mn	Si	Cr	Ni	Mo	Cu	S	P
Requirements	≤0.15	0.5-2.50	≤1.00	28.0-32.0	8-10.5	≤0.75	≤0.75	≤0.03	≤0.04
Typical Results	0.085	1.11	0.78	29.39	9.97	0.16	0.2	0.011	0.028

Mechanical Properties of Deposited Metal (AW)
items	Tensile Strength Rm (MPa)	Elongation A4(%)
Requirements	≥660	≥15
Typical Results	785	26

 

E316L-16
items	C	Mn	Si	Cr	Ni	Mo	Cu	S	P
Requirements	≤0.04	0.5-2.50	≤1.00	17.0-20.0	11-14	2-3	≤0.75	≤0.03	≤0.04
Typical Results	0.030	1.01	0.68	19.01	11.82	2.46	0.08	0.015	0.025

Mechanical Properties of Deposited Metal (AW)
items	Tensile Strength Rm (MPa)	Elongation A4(%)
Requirements	≥490	≥25
Typical Results	580	45

Attention:

1.The electrode must be re-dry by 320ºC-350ºC for 1 hour before welding,
2.The rust, oil, water and other impurities of the weld area must be removed before welding.
3.DC*is better than AC, lower heat input is suggested, the temperature of preheat and interpass keep under 150ºC