Factory Direct Sales Er70s-6 Welding Wire with High Quality

• Customization: Available
• Type: Rolling Wire
• Material: Carbon Steel
• Model NO.: ER70S-6
• Flux Containing: Not Containing Flux
• Slag Characteristic: Acidic
• Sample: Avaiable
• Quality: High Quality
• OEM: Accept
• After-Sales Service: Perfect
• Transport Package: 1kg/5kg/15kg/20kg/Spool, 250kg/350kg
• Specification: 0.8/0.9/1.0/1.2/1.6mm
• Trademark: JINYUAN
• Origin: Hebei, China
• HS Code: 72292000

Product Description

 

Product Description

MODEL		ER70S-6
SIZE(mm)		0.8-1.6
STANDARD		AWS A5.18 ER70S-6
SHIELDED GAS		CO2
TYPE OF CURRENT		DC+
TYPICAL CHEMICAL COMPOSITION OF DEPOSITED METAL(%)		C:0.071 Mn:1.49 Si:0.88 S:0.011 P:0.01
TYPICAL MECHANICAL PROPERTIES OF DEPOSITED METAL	Rm(MPa)	545
	Rel(MPa)	400
	A (%)	27
	KV2(J)	114(- 30°C)
APPLICATION		Welding of carbon steel, low alloy steel and 500Mpa grade low alloy high intensity steel structures, etc. Such as vehicle, building, bridge, ship building, pressure vessel industry and pipeline etc

Applications:
It can be used in tee welding of carbon steel and low alloy steel in the corresponding strength grade, which can be used in engineering machinery, ship, vehicle manufacturing, petrochemical and other industries.

Characteristics:
Wire THQ-50C is 500MPa level carbon steel wire. It take CO2 or 80%Ar+20%CO2 gas shielded arc welding. The welding spatter is small, and it has beautiful appearance, high cladding efficiency and small weld metal porosity sensibility. The welding technology of all positions is good.

Chemical Composition of the Wire (%)

	C	Mn	Si	S	P	Ni	Cr	Mo	V	Cu
Standard	0.06-0.15	1.40-1.85	0.80-1.15	≤0.035	≤0.025	≤0.15	≤0.15	≤0.15	≤0.03	≤0.50
Typical	0.078	1.53	0.85	0.010	0.010	0.029	0.022	0.008	0.010	0.12

 

Mechanical Properties of Deposited Metal (AW)

	Yield strength ReL(Mpa)	Tensile Strength Rm(Mpa)	Elongation A4(%)	Impact Value (J)			Shield Gas
				-20ºC	-30ºC	-40ºC	CO2
Standard	≥420	≥500	≥22	≥47	≥27	_	Purity ≥99.98%
Typical	430	550	30	102	89	70

Recommended Current (DC+ )

Diameter(mm)	0.6	0.8	0.9	1.0	1.2	1.6
Current (A )	40-120	40-140	40-180	50-220	80-350	120-550

Notice:
1) To avoid rust the wire must be kept in dry condition and keep the package in good condition also before welding.
2) To avoid welding defect the shield gas should be pure particularly no moisture in it.
3) The surfaces to be welded must be cleaned away impurities of oil contamination, rust, moisture and so on.
4) The welding conditions mentioned above for reference only and it is better to do a welding procedure qualiffcation according to project before put it into formal welding.

 

Detailed Photos

 

Certifications

 

Company Profile

 

FAQ

1. Are you manufacturer?
We have more than 20 years produce experience.and now my factory is producing annealed wire, galvanized wire, nails, welding
electrode and wire meshes. Welcome to inquiry.

2. how can we guarantee quality?
Always a pre-production sample before mass production;
Always final Inspection before shipment;

3.what can you buy from us?
Galvanized Wire,Annealed Wire,Nails,Welding Electrode,Wire Meshes

4. why should you buy from us not from other suppliers?
1). High Quality Products
2). 22 Years Production Experirance
3). 8 Production Line and 60 Drawing Wire Machine
4). Short Delivery Time
5). OEM