Premium Jinyuan E71t1 Welding Wire for Flux Cored Applications

• Customization: Available
• Type: Flux-cored Wire
• Material: High Tensile Strength Steels
• Model NO.: E71T1
• Flux Containing: Containing Flux
• Slag Characteristic: Acidic
• Extended Length: 15-25mm
• Transport Package: Customized
• Specification: 1/5/15/20 KG
• Trademark: JINYUAN
• Origin: China
• HS Code: 7229200000
• Production Capacity: 1000 Tons Per Month

Product Description

Discover unparalleled welding excellence with our Premium JINYUAN E71T1 Welding Wire, designed for superior flux core applications. This remarkable welding wire showcases exceptional performance and outstanding efficiency, especially suitable for vertical down welding techniques. It is the preferred choice for a multitude of fabrication needs, including structures assembled with equivalent mild steels and superior 490MPa grade high tensile strength steels. Whether it's for ships, pressure vessels, machinery, petrochemical industry equipment, or magnificent bridges, our welding wire delivers reliable and robust results every time.

Basic Info.

Model NO.	E71T1
Size(mm)	0.8~1.6mm
Slag Characteristic	Acidic
Shielded Gas	CO2
Type Of Current	DC+
Specification	1/5/15/20kg
Flux Containing	Containing Flux
Application	Structures fabricated by equivalent mild steels and 490Mpa grade high tensile strength steels. such as ships, pressure vessels, machineries, petrochemical industry equipments and so on.
Origin	China

Product Specification

E71T1
E71T1 Welding Wire Chemical Composition of Deposited Metal (%)
Composition	C	Mn	Si	S	P
Standard	≤0.18	≤1.75	≤0.90	≤0.03	≤0.03
Typical	0.055	1.35	0.40	0.009	0.018

E71T1 Welding Wire Mechanical Properties of Deposited Metal(AW)
	Yield Strength ReH(Mpa)	Tensile Strength Rm (Mpa)	Elongation A4(%)	Impact Value(J)	Shield Gas
				-20ºC	CO2
Standard	≥400	≥480	≥22	≥27	purity≥99.98%
Typical	440	535	32	110

E71TGS
E71TGS Welding Wire Chemical Composition of Deposited Metal (%)
items	C	Mn	Si	S	P	Ni	Al
Standard value	-	≤1.75	≤0.92	≤0.03	≤0.03	≤0.50	≤1.80

 

E71TGS Welding Wire Mechanical Properties of Deposited Metal(AW)
Test items	Yield Strength Rm(Mpa)	Tensile Strength Rm(Mpa)	Elongation A4(%)
Standard valve	≥400	≥480	-

Attention
For optimal results, ensure the shield gas flow rate is maintained between 20L to 50L per minute during the welding process.
Maintain a wire extension of 15mm to 25mm to achieve the best welding outcomes.
Prior to welding, meticulously clean the surfaces to eliminate impurities such as oil contamination, rust, and moisture to ensure superior adhesion and flawless welds.